Karakteristik Fisik FIBREALUM

Characteristic	Value	Methods of Testing
Density (kg/m3)	1,51	ASTM D792-2000
Coefficient of thermal expansion (µm/ m 0C) a) α1 (-50 0C ÷ 0 0C) b) α2 (60 0C ÷ 110 0C)	81,5 483	ASTM E831-2000
Water absorption (%) a) weight gain (%) b) material dissolved (%)	0,41 0,37 0,04	ASTM D570-2005
Thermal conductivity (W/ m K)	0,158	ASTM C177-2004
Heat distortion temperature (0C)	> 260	ASTM D648-2007
Operating temperature (0C)	-20 ÷ 65
Glass fiber content (%)	30	ASTM D2584-2004
Fire in the horizontal direction	CLASS HB	UL 94
Resistance to fire from outside	CLASS C	ASTM E108-2004

Karakteristik Mekanik FIBREALUM

Characteristic	Value	Methods of Testing
Barcol hardness	> 50	ASTM D2583-2001
Impact strength (Izod) (J/m)	927	ASTM D256-2002
Shear strength (punch) (MPa)	52,3	ASTM D732-2002
Compressive strength (MPa)	135	ASTM D695-2004
Weather resistance (simulation testing in the laboratory)		ASTM G154-2006
Tensile strength (MPa) a) initial b) 1000 h accelerated weathering	113 ÷ 129 104 ÷ 128	ASTM D882-2002
Tensile modulus (MPa) a) initial b) 1000 h accelerated weathering	2271 ÷ 3059 2386 ÷ 2601	ASTM D882-2002
Flexural strength (MPa) a) initial b) 1000 h accelerated weathering	241 ÷ 245 210 ÷ 230	ASTM D790-2003
Flexural modulus (MPa) a) initial b) 1000 h accelerated weathering	6408 ÷ 6567 6611 ÷ 7547	ASTM D790-2003
Color measurement, DE a) 500 h accelerated weathering b) 1000 h accelerated weathering	12,3 ÷ 18,0 13,5 ÷ 19,8	ASTM E1348-2007